可熔性聚四氟乙烯(P-65P) 1.PFA(可溶性聚四氟乙烯)在化学，电气及热性能与PTFE相近。耐高温,不粘特性,优良的耐化学性，耐气候和老 化及介电性能。还可用于挤出、注塑、吹塑、传递模塑及模压等方法加工。 2.适用范围:目前国内主要用于防腐防酸碱注塑件、高温电线电缆、防酸碱内衬件，吹塑制品、耐磨件、
密封件、绝缘件和医疗器械零件。广泛应用于半导体行业、以及医疗、化工防腐、汽车等领域。 PFA技术参数 | Property (特性) | Units (单位) | Test Method (测试方法) | P-66P | P-65P | P-63P | P-62XP | Melt Flow Rate (熔融指数) | g/10min | D-3159 | 2.0 | 5.0 | 12.0 | 30.0 | Melting Point (熔点) | ℃ | D-3159 | 310 | 310 | 310 | 310 | Specific Gravity(密度) | g/cm³ | D-792 | 2.14 | 2.14 | 2.14 | 2.14 | Hardness(硬度，邵氏D) | Shore D | D-2240 | 60 | 60 | 60 | 60 | Tensile Strength (23℃) (拉伸强度) | psi | D-638 | 5,655 | 5,220 | 4,640 | 4,640 | Tensile Elongation (23℃) (断裂伸长率) | % | D-638 | 340 | 390 | 410 | 410 | Tensile Strength (250℃) (拉伸强度) | psi | D-638 | 2,000 | 1740 | 1300 | 1000 | Tensile Elongation (250℃) (断裂伸长率) | % | D-638 | 740 | 680 | 600 | 580 | Flexural Modulus (23℃) (弯曲模量) | psi | D-790 | 87000 | 88000 | 91000 | 101500 | Heat Deflection Temp. (66 psi) (热变形温度) | ℃ | D-648 | 91 | | 92 | 93 | Heat Deflection Temp. (264psi) (热变形温度) | ℃ | D-648 | 56 | | 57 | 57 | Notched Izod Impact (23℃) (缺口冲击强度) | ft-lb/in | C-256 | No Break | No Break | No Break | No Break | Embrittlement Temperature(脆化温度) | ℃ | D-764 | | | | | CLTE (0 – 100℃) (线热膨胀系数) | in/in/℉ | D-696 | 7.2 x 10-5 | 7.2 x 10-5 | 7.2 x 10-5 | 7.2 x 10-5 | Water Absorption (24 hours) (吸水率) | % | D-570 | <0.03 | <0.03 | <0.03 | <0.03 | Dielectric Constant (1 mHz at 23℃) (介电常数) | | D-150 | 2.07 | 2.07 | 2.07 | 2.07 | Volume Resistivity(体积电阻率) | Ω-cm | D-257 | >1018 | >1018 | >1018 | >1018 | Dielectric Strength (10 mil film) (介电强度) | volts/mil | D-149 | 1900 | 1900 | 1900 | 1900 | Heat of Combustion(燃烧热) | BTU/lb | D-240 | 2200 | 2200 | 2200 | 2200 | Specific Heat(比热) | cal/g-℃ | | 0.25 | 0.25 | 0.25 | 0.25 | Oxygen Index(极限氧指数) | % | D-2863 | >95 | >95 | >95 | >95 | Flame Rating(阻燃性) | | UL-94 | V-0 | V-0 | V-0 | V-0 | Upper Service Temperature(最高连续工作温度) | ℃ | UL-746 | 260 | 260 | 260 | 260 | MIT Flex Life(耐拆度) | Cycles | D-2176 | 500000 | 200000 | 250000 | 180000 | Application(应用) | | | 注塑/挤出/模压 | 注塑/挤出 | 注塑/挤出 | 注塑/高速挤出 | | | | | | | | | | | | | | | | | | | | | | |